ASTM B596 Au-Cu vs. ASTM B563 Pd-Ag-Cu
Both ASTM B596 Au-Cu and ASTM B563 Pd-Ag-Cu are otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM B596 Au-Cu and the bottom bar is ASTM B563 Pd-Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 4.3 to 17 | |
| 7.0 to 17 |
| Poisson's Ratio | 0.41 | |
| 0.37 |
| Shear Modulus, GPa | 36 | |
| 37 |
| Shear Strength, MPa | 280 to 360 | |
| 470 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 620 | |
| 760 to 1170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 150 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1180 |
| Melting Onset (Solidus), °C | 930 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 260 |
| Thermal Expansion, µm/m-K | 14 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 5.6 to 6.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.7 | |
| 4.6 to 5.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 18 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 8.5 | |
| 14 |
| Strength to Weight: Axial, points | 6.8 to 9.4 | |
| 19 to 30 |
| Strength to Weight: Bending, points | 7.1 to 8.8 | |
| 17 to 22 |
| Thermal Shock Resistance, points | 22 to 30 | |
| 39 to 61 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 9.0 to 11 | |
| 15.5 to 16.5 |
| Gold (Au), % | 89 to 91 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.8 to 1.2 |
| Palladium (Pd), % | 0 | |
| 43 to 45 |
| Platinum (Pt), % | 0 | |
| 0.8 to 1.2 |
| Silver (Ag), % | 0 | |
| 37 to 39 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |