ASTM B596 Au-Cu vs. Solder Alloy 136

Both ASTM B596 Au-Cu and solder alloy 136 are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM B596 Au-Cu and the bottom bar is solder alloy 136.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
25
Elongation at Break, % 4.3 to 17
19
Poisson's Ratio 0.41
0.42
Shear Modulus, GPa 36
8.9
Tensile Strength: Ultimate (UTS), MPa 450 to 620
34

Thermal Properties

Latent Heat of Fusion, J/g 77
34
Melting Completion (Liquidus), °C 1060
260
Melting Onset (Solidus), °C 930
190
Specific Heat Capacity, J/kg-K 150
150
Thermal Expansion, µm/m-K 14
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 14
9.2
Electrical Conductivity: Equal Weight (Specific), % IACS 6.7
8.0

Otherwise Unclassified Properties

Density, g/cm3 18
10

Common Calculations

Stiffness to Weight: Axial, points 3.1
1.4
Stiffness to Weight: Bending, points 8.5
9.5
Strength to Weight: Axial, points 6.8 to 9.4
0.92
Strength to Weight: Bending, points 7.1 to 8.8
2.3
Thermal Shock Resistance, points 22 to 30
3.6

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0.5 to 2.0
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 9.0 to 11
0 to 0.080
Gold (Au), % 89 to 91
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
71.9 to 75
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 0
0 to 0.1
Tin (Sn), % 0
24.5 to 25.5
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.4
0