ASTM B617 Coin Silver vs. 6016 Aluminum
ASTM B617 coin silver belongs to the otherwise unclassified metals classification, while 6016 aluminum belongs to the aluminum alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is 6016 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 75 | |
| 69 |
| Elongation at Break, % | 1.1 to 22 | |
| 11 to 27 |
| Poisson's Ratio | 0.37 | |
| 0.33 |
| Shear Modulus, GPa | 28 | |
| 26 |
| Shear Strength, MPa | 180 to 290 | |
| 130 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 520 | |
| 200 to 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 410 |
| Melting Completion (Liquidus), °C | 870 | |
| 660 |
| Melting Onset (Solidus), °C | 780 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 900 |
| Thermal Expansion, µm/m-K | 19 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 83 | |
| 48 to 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 72 | |
| 160 to 180 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 2.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 51 |
| Strength to Weight: Axial, points | 7.7 to 14 | |
| 21 to 29 |
| Strength to Weight: Bending, points | 9.3 to 14 | |
| 29 to 35 |
| Thermal Shock Resistance, points | 14 to 25 | |
| 9.1 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 96.4 to 98.8 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 9.0 to 10.4 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0.25 to 0.6 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 | |
| 1.0 to 1.5 |
| Silver (Ag), % | 89.6 to 91 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.060 | |
| 0 to 0.15 |