ASTM B617 Coin Silver vs. EN 1.7386 Steel
ASTM B617 coin silver belongs to the otherwise unclassified metals classification, while EN 1.7386 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is EN 1.7386 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 75 | |
| 190 |
| Elongation at Break, % | 1.1 to 22 | |
| 18 to 21 |
| Poisson's Ratio | 0.37 | |
| 0.28 |
| Shear Modulus, GPa | 28 | |
| 75 |
| Shear Strength, MPa | 180 to 290 | |
| 340 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 520 | |
| 550 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 120 | |
| 270 |
| Melting Completion (Liquidus), °C | 870 | |
| 1450 |
| Melting Onset (Solidus), °C | 780 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 250 | |
| 480 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 83 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 72 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 25 |
| Strength to Weight: Axial, points | 7.7 to 14 | |
| 20 to 24 |
| Strength to Weight: Bending, points | 9.3 to 14 | |
| 19 to 22 |
| Thermal Shock Resistance, points | 14 to 25 | |
| 15 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.040 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 0 | |
| 8.0 to 10 |
| Copper (Cu), % | 9.0 to 10.4 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.050 | |
| 86.8 to 90.5 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0.25 to 1.0 |
| Silver (Ag), % | 89.6 to 91 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |
| Residuals, % | 0 to 0.060 | |
| 0 |