MakeItFrom.com
Menu (ESC)

ASTM B617 Coin Silver vs. Grade 15 Babbitt Metal

Both ASTM B617 coin silver and grade 15 Babbitt Metal are otherwise unclassified metals. There are 11 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is grade 15 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 75
23
Poisson's Ratio 0.37
0.4
Shear Modulus, GPa 28
8.2

Thermal Properties

Latent Heat of Fusion, J/g 120
46
Melting Completion (Liquidus), °C 870
280
Melting Onset (Solidus), °C 780
250
Specific Heat Capacity, J/kg-K 250
140
Thermal Expansion, µm/m-K 19
26

Otherwise Unclassified Properties

Density, g/cm3 10
10

Common Calculations

Stiffness to Weight: Axial, points 4.1
1.2
Stiffness to Weight: Bending, points 14
9.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0 to 0.0050
Antimony (Sb), % 0
14.5 to 17.5
Arsenic (As), % 0
0.8 to 1.4
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0 to 0.050
0 to 0.050
Copper (Cu), % 9.0 to 10.4
0 to 0.6
Iron (Fe), % 0 to 0.050
0 to 0.1
Lead (Pb), % 0 to 0.030
79 to 83.9
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.020
0
Silver (Ag), % 89.6 to 91
0
Tin (Sn), % 0
0.8 to 1.2
Zinc (Zn), % 0 to 0.060
0 to 0.0050
Residuals, % 0 to 0.060
0