ASTM B617 Coin Silver vs. Solder Alloy 102

Both ASTM B617 coin silver and solder alloy 102 are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is solder alloy 102.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 75
38
Elongation at Break, % 1.1 to 22
48
Poisson's Ratio 0.37
0.39
Shear Modulus, GPa 28
14
Tensile Strength: Ultimate (UTS), MPa 290 to 520
31

Thermal Properties

Latent Heat of Fusion, J/g 120
46
Melting Completion (Liquidus), °C 870
180
Melting Onset (Solidus), °C 780
180
Specific Heat Capacity, J/kg-K 250
190
Thermal Expansion, µm/m-K 19
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 83
12
Electrical Conductivity: Equal Weight (Specific), % IACS 72
13

Otherwise Unclassified Properties

Density, g/cm3 10
8.8

Common Calculations

Stiffness to Weight: Axial, points 4.1
2.4
Stiffness to Weight: Bending, points 14
13
Strength to Weight: Axial, points 7.7 to 14
1.0
Strength to Weight: Bending, points 9.3 to 14
2.5
Thermal Shock Resistance, points 14 to 25
2.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0 to 0.0010
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.050
Cadmium (Cd), % 0 to 0.050
0 to 0.0020
Copper (Cu), % 9.0 to 10.4
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.050
0 to 0.020
Lead (Pb), % 0 to 0.030
36 to 37.5
Nickel (Ni), % 0 to 0.010
0 to 0.010
Phosphorus (P), % 0 to 0.020
0
Silver (Ag), % 89.6 to 91
0 to 0.1
Tin (Sn), % 0
62.5 to 63.5
Zinc (Zn), % 0 to 0.060
0 to 0.0010
Residuals, % 0 to 0.060
0