ASTM B617 Coin Silver vs. Solder Alloy 137

Both ASTM B617 coin silver and solder alloy 137 are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is solder alloy 137.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 75
24
Elongation at Break, % 1.1 to 22
19
Poisson's Ratio 0.37
0.42
Shear Modulus, GPa 28
8.3
Tensile Strength: Ultimate (UTS), MPa 290 to 520
34

Thermal Properties

Latent Heat of Fusion, J/g 120
33
Melting Completion (Liquidus), °C 870
270
Melting Onset (Solidus), °C 780
190
Specific Heat Capacity, J/kg-K 250
150
Thermal Expansion, µm/m-K 19
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 83
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 72
7.7

Otherwise Unclassified Properties

Density, g/cm3 10
10

Common Calculations

Stiffness to Weight: Axial, points 4.1
1.3
Stiffness to Weight: Bending, points 14
9.2
Strength to Weight: Axial, points 7.7 to 14
0.9
Strength to Weight: Bending, points 9.3 to 14
2.2
Thermal Shock Resistance, points 14 to 25
3.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0 to 0.0010
Antimony (Sb), % 0
0.5 to 3.0
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0 to 0.050
0 to 0.0050
Copper (Cu), % 9.0 to 10.4
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.050
0 to 0.020
Lead (Pb), % 0 to 0.030
75.9 to 80
Nickel (Ni), % 0 to 0.010
0 to 0.010
Phosphorus (P), % 0 to 0.020
0
Silver (Ag), % 89.6 to 91
0 to 0.1
Tin (Sn), % 0
19.5 to 20.5
Zinc (Zn), % 0 to 0.060
0 to 0.0010
Residuals, % 0 to 0.060
0