ASTM B617 Coin Silver vs. Z13004 Zinc

ASTM B617 coin silver belongs to the otherwise unclassified metals classification, while Z13004 zinc belongs to the zinc alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM B617 coin silver and the bottom bar is Z13004 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 75
87
Elongation at Break, % 1.1 to 22
30
Poisson's Ratio 0.37
0.25
Shear Modulus, GPa 28
35
Tensile Strength: Ultimate (UTS), MPa 290 to 520
93

Thermal Properties

Latent Heat of Fusion, J/g 120
110
Melting Completion (Liquidus), °C 870
410
Melting Onset (Solidus), °C 780
390
Specific Heat Capacity, J/kg-K 250
390
Thermal Expansion, µm/m-K 19
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 83
27
Electrical Conductivity: Equal Weight (Specific), % IACS 72
37

Otherwise Unclassified Properties

Density, g/cm3 10
6.6

Common Calculations

Stiffness to Weight: Axial, points 4.1
7.4
Stiffness to Weight: Bending, points 14
23
Strength to Weight: Axial, points 7.7 to 14
3.9
Strength to Weight: Bending, points 9.3 to 14
7.0
Thermal Shock Resistance, points 14 to 25
2.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0 to 0.0020
Cadmium (Cd), % 0 to 0.050
0 to 0.0030
Copper (Cu), % 9.0 to 10.4
0 to 0.0030
Iron (Fe), % 0 to 0.050
0 to 0.0030
Lead (Pb), % 0 to 0.030
0 to 0.0030
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.020
0
Silver (Ag), % 89.6 to 91
0
Tin (Sn), % 0
0 to 0.0010
Zinc (Zn), % 0 to 0.060
99.985 to 100
Residuals, % 0 to 0.060
0