ASTM B628 Ag-Cu vs. 2024 Aluminum

ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while 2024 aluminum belongs to the aluminum alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is 2024 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
71
Elongation at Break, % 1.1 to 17
4.0 to 16
Poisson's Ratio 0.36
0.33
Shear Modulus, GPa 31
27
Shear Strength, MPa 210 to 430
130 to 320
Tensile Strength: Ultimate (UTS), MPa 350 to 760
200 to 540

Thermal Properties

Latent Heat of Fusion, J/g 140
390
Melting Completion (Liquidus), °C 780
640
Melting Onset (Solidus), °C 780
500
Specific Heat Capacity, J/kg-K 280
880
Thermal Expansion, µm/m-K 19
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 84
30
Electrical Conductivity: Equal Weight (Specific), % IACS 75
90

Otherwise Unclassified Properties

Density, g/cm3 10
3.0

Common Calculations

Stiffness to Weight: Axial, points 4.6
13
Stiffness to Weight: Bending, points 14
46
Strength to Weight: Axial, points 9.5 to 21
18 to 50
Strength to Weight: Bending, points 11 to 18
25 to 49
Thermal Shock Resistance, points 16 to 34
8.6 to 24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
90.7 to 94.7
Cadmium (Cd), % 0 to 0.050
0
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 26.6 to 29
3.8 to 4.9
Iron (Fe), % 0 to 0.050
0 to 0.5
Lead (Pb), % 0 to 0.030
0
Magnesium (Mg), % 0
1.2 to 1.8
Manganese (Mn), % 0
0.3 to 0.9
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 71 to 73
0
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 0 to 0.060
0 to 0.25
Zirconium (Zr), % 0
0 to 0.2
Residuals, % 0 to 0.21
0 to 0.15

Comparable Variants