ASTM B628 Ag-Cu vs. AISI 410Cb Stainless Steel

ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while AISI 410Cb stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is AISI 410Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
190
Elongation at Break, % 1.1 to 17
15
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 31
76
Shear Strength, MPa 210 to 430
340 to 590
Tensile Strength: Ultimate (UTS), MPa 350 to 760
550 to 960

Thermal Properties

Latent Heat of Fusion, J/g 140
270
Melting Completion (Liquidus), °C 780
1450
Melting Onset (Solidus), °C 780
1400
Specific Heat Capacity, J/kg-K 280
480
Thermal Expansion, µm/m-K 19
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 84
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 75
3.3

Otherwise Unclassified Properties

Density, g/cm3 10
7.7

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 14
25
Strength to Weight: Axial, points 9.5 to 21
20 to 35
Strength to Weight: Bending, points 11 to 18
19 to 28
Thermal Shock Resistance, points 16 to 34
20 to 35

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.18
Chromium (Cr), % 0
11 to 13
Copper (Cu), % 26.6 to 29
0
Iron (Fe), % 0 to 0.050
84.5 to 89
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0 to 0.010
0
Niobium (Nb), % 0
0.050 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 71 to 73
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.060
0
Residuals, % 0 to 0.21
0

Comparable Variants