ASTM B628 Ag-Cu vs. EN 1.5537 Steel

ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while EN 1.5537 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is EN 1.5537 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
190
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 31
73
Tensile Strength: Ultimate (UTS), MPa 350 to 760
520 to 1760

Thermal Properties

Latent Heat of Fusion, J/g 140
250
Melting Completion (Liquidus), °C 780
1460
Melting Onset (Solidus), °C 780
1420
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 84
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 75
8.2

Otherwise Unclassified Properties

Density, g/cm3 10
7.8

Common Calculations

Stiffness to Weight: Axial, points 4.6
13
Stiffness to Weight: Bending, points 14
24
Strength to Weight: Axial, points 9.5 to 21
18 to 63
Strength to Weight: Bending, points 11 to 18
18 to 41
Thermal Shock Resistance, points 16 to 34
15 to 52

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Boron (B), % 0
0.00080 to 0.0050
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.33 to 0.38
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 26.6 to 29
0 to 0.25
Iron (Fe), % 0 to 0.050
97.6 to 98.9
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0.8 to 1.1
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0
0 to 0.3
Silver (Ag), % 71 to 73
0
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 0 to 0.060
0
Residuals, % 0 to 0.21
0