ASTM B628 Ag-Cu vs. Grade 8 Babbitt Metal

Both ASTM B628 Ag-Cu and grade 8 Babbitt Metal are otherwise unclassified metals. There are 11 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is grade 8 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
24
Poisson's Ratio 0.36
0.41
Shear Modulus, GPa 31
8.5

Thermal Properties

Latent Heat of Fusion, J/g 140
46
Melting Completion (Liquidus), °C 780
270
Melting Onset (Solidus), °C 780
240
Specific Heat Capacity, J/kg-K 280
150
Thermal Expansion, µm/m-K 19
24

Otherwise Unclassified Properties

Density, g/cm3 10
10

Common Calculations

Stiffness to Weight: Axial, points 4.6
1.3
Stiffness to Weight: Bending, points 14
9.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0 to 0.0050
Antimony (Sb), % 0
14 to 16
Arsenic (As), % 0
0.3 to 0.6
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0 to 0.050
0 to 0.050
Copper (Cu), % 26.6 to 29
0 to 0.5
Iron (Fe), % 0 to 0.050
0 to 0.1
Lead (Pb), % 0 to 0.030
77.1 to 81.2
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.030
0
Silver (Ag), % 71 to 73
0
Tin (Sn), % 0
4.5 to 5.5
Zinc (Zn), % 0 to 0.060
0 to 0.0050
Residuals, % 0 to 0.21
0