ASTM B628 Ag-Cu vs. C47000 Brass

ASTM B628 Ag-Cu belongs to the otherwise unclassified metals classification, while C47000 brass belongs to the copper alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is ASTM B628 Ag-Cu and the bottom bar is C47000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
100
Elongation at Break, % 1.1 to 17
36
Poisson's Ratio 0.36
0.3
Shear Modulus, GPa 31
40
Tensile Strength: Ultimate (UTS), MPa 350 to 760
380

Thermal Properties

Latent Heat of Fusion, J/g 140
170
Melting Completion (Liquidus), °C 780
900
Melting Onset (Solidus), °C 780
890
Specific Heat Capacity, J/kg-K 280
390
Thermal Expansion, µm/m-K 19
21

Otherwise Unclassified Properties

Density, g/cm3 10
8.0

Common Calculations

Stiffness to Weight: Axial, points 4.6
7.2
Stiffness to Weight: Bending, points 14
20
Strength to Weight: Axial, points 9.5 to 21
13
Strength to Weight: Bending, points 11 to 18
15
Thermal Shock Resistance, points 16 to 34
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0 to 0.010
Cadmium (Cd), % 0 to 0.050
0
Copper (Cu), % 26.6 to 29
57 to 61
Iron (Fe), % 0 to 0.050
0
Lead (Pb), % 0 to 0.030
0 to 0.050
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.030
0
Silver (Ag), % 71 to 73
0
Tin (Sn), % 0
0.25 to 1.0
Zinc (Zn), % 0 to 0.060
37.5 to 42.8
Residuals, % 0 to 0.21
0 to 0.4