ASTM B631 Class A vs. C46200 Brass

ASTM B631 class A belongs to the otherwise unclassified metals classification, while C46200 brass belongs to the copper alloys. There are 14 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is ASTM B631 class A and the bottom bar is C46200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
100
Poisson's Ratio 0.3
0.31
Shear Modulus, GPa 85 to 86
40

Thermal Properties

Latent Heat of Fusion, J/g 160
170
Melting Completion (Liquidus), °C 2680 to 2690
840
Specific Heat Capacity, J/kg-K 160
380
Thermal Conductivity, W/m-K 420
110
Thermal Expansion, µm/m-K 11
20

Otherwise Unclassified Properties

Density, g/cm3 15
8.1
Embodied Carbon, kg CO2/kg material 43
2.7
Embodied Energy, MJ/kg 670
46

Common Calculations

Stiffness to Weight: Axial, points 8.5
7.2
Stiffness to Weight: Bending, points 14
19
Thermal Diffusivity, mm2/s 180
35