ASTM B631 Class B vs. ASTM B631 Class C
Both ASTM B631 class B and ASTM B631 class C are otherwise unclassified metals.
For each property being compared, the top bar is ASTM B631 class B and the bottom bar is ASTM B631 class C.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 180 to 190 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Rockwell B Hardness | 53 to 85 | |
| 43 to 68 |
| Shear Modulus, GPa | 78 to 79 | |
| 66 to 71 |
Thermal Properties
| Latent Heat of Fusion, J/g | 150 | |
| 140 to 150 |
| Melting Completion (Liquidus), °C | 2460 to 2480 | |
| 2090 to 2230 |
| Specific Heat Capacity, J/kg-K | 170 | |
| 180 |
| Thermal Conductivity, W/m-K | 450 | |
| 450 to 490 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 to 53 | |
| 55 to 63 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 32 to 34 | |
| 36 to 43 |
Otherwise Unclassified Properties
| Density, g/cm3 | 14 | |
| 13 to 14 |
| Embodied Carbon, kg CO2/kg material | 49 | |
| 55 to 59 |
| Embodied Energy, MJ/kg | 760 | |
| 860 to 920 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.1 | |
| 7.4 to 7.6 |
| Stiffness to Weight: Bending, points | 14 | |
| 14 |
| Thermal Diffusivity, mm2/s | 190 | |
| 180 to 200 |