ASTM B685 Alloy vs. AWS BAg-13a
Both ASTM B685 alloy and AWS BAg-13a are otherwise unclassified metals. They have 40% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ASTM B685 alloy and the bottom bar is AWS BAg-13a.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 92 |
| Poisson's Ratio | 0.37 | |
| 0.36 |
| Shear Modulus, GPa | 43 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 1060 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 160 |
| Melting Completion (Liquidus), °C | 1230 | |
| 890 |
| Melting Onset (Solidus), °C | 1200 | |
| 770 |
| Specific Heat Capacity, J/kg-K | 300 | |
| 300 |
| Thermal Expansion, µm/m-K | 14 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 9.8 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.1 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 15 | |
| 15 |
| Strength to Weight: Axial, points | 17 to 27 | |
| 5.1 |
| Strength to Weight: Bending, points | 16 to 21 | |
| 7.2 |
| Thermal Shock Resistance, points | 28 to 46 | |
| 7.5 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 39.5 to 40.5 | |
| 40.4 to 43.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 1.5 to 2.5 |
| Palladium (Pd), % | 59 to 60.5 | |
| 0 |
| Silver (Ag), % | 0 to 0.1 | |
| 55 to 57 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.15 |