ASTM B780 Alloy vs. 90-silver 10-nickel
Both ASTM B780 alloy and 90-silver 10-nickel are otherwise unclassified metals. They have 76% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is 90-silver 10-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 82 |
| Poisson's Ratio | 0.36 | |
| 0.36 |
| Shear Modulus, GPa | 30 | |
| 30 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 590 | |
| 250 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 130 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 260 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 70 to 76 | |
| 90 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 to 68 | |
| 79 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.5 | |
| 4.4 |
| Stiffness to Weight: Bending, points | 14 | |
| 14 |
| Strength to Weight: Axial, points | 9.1 to 16 | |
| 6.7 to 11 |
| Strength to Weight: Bending, points | 11 to 15 | |
| 8.5 to 12 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 11 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 23.5 to 25.7 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0.35 to 0.65 | |
| 8.8 to 11 |
| Silver (Ag), % | 74 to 76 | |
| 89 to 91 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |