ASTM B780 Alloy vs. AISI 301LN Stainless Steel

ASTM B780 alloy belongs to the otherwise unclassified metals classification, while AISI 301LN stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is AISI 301LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
200
Elongation at Break, % 1.1 to 9.1
23 to 51
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 30
77
Shear Strength, MPa 200 to 340
450 to 670
Tensile Strength: Ultimate (UTS), MPa 330 to 590
630 to 1060

Thermal Properties

Latent Heat of Fusion, J/g 140
280
Specific Heat Capacity, J/kg-K 270
480
Thermal Expansion, µm/m-K 18
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 70 to 76
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 62 to 68
2.7

Otherwise Unclassified Properties

Density, g/cm3 10
7.8

Common Calculations

Stiffness to Weight: Axial, points 4.5
14
Stiffness to Weight: Bending, points 14
25
Strength to Weight: Axial, points 9.1 to 16
22 to 38
Strength to Weight: Bending, points 11 to 15
21 to 30
Thermal Shock Resistance, points 16 to 29
14 to 24

Alloy Composition

Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 23.5 to 25.7
0
Iron (Fe), % 0 to 0.050
70.7 to 77.9
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0.35 to 0.65
6.0 to 8.0
Nitrogen (N), % 0
0.070 to 0.2
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 74 to 76
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.060
0

Comparable Variants