ASTM B780 Alloy vs. ASTM B522 Class II
Both ASTM B780 alloy and ASTM B522 class II are otherwise unclassified metals. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is ASTM B522 class II.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 96 |
| Elongation at Break, % | 1.1 to 9.1 | |
| 1.1 to 28 |
| Poisson's Ratio | 0.36 | |
| 0.41 |
| Shear Modulus, GPa | 30 | |
| 34 |
| Shear Strength, MPa | 200 to 340 | |
| 180 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 590 | |
| 280 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 77 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 160 |
| Thermal Expansion, µm/m-K | 18 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 70 to 76 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 to 68 | |
| 5.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.5 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 14 | |
| 8.9 |
| Strength to Weight: Axial, points | 9.1 to 16 | |
| 4.4 to 7.8 |
| Strength to Weight: Bending, points | 11 to 15 | |
| 5.5 to 8.0 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 13 to 24 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 |
| Copper (Cu), % | 23.5 to 25.7 | |
| 0 |
| Gold (Au), % | 0 | |
| 68.5 to 69.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0.35 to 0.65 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 5.5 to 6.5 |
| Silver (Ag), % | 74 to 76 | |
| 24.5 to 25.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.26 |