ASTM B780 alloy belongs to the otherwise unclassified metals classification, while ASTM grade HF steel belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is ASTM grade HF steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
200
Elongation at Break, % 1.1 to 9.1
29
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 30
77
Tensile Strength: Ultimate (UTS), MPa 330 to 590
550

Thermal Properties

Latent Heat of Fusion, J/g 140
300
Specific Heat Capacity, J/kg-K 270
480
Thermal Expansion, µm/m-K 18
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 70 to 76
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 62 to 68
2.4

Otherwise Unclassified Properties

Density, g/cm3 10
7.7

Common Calculations

Stiffness to Weight: Axial, points 4.5
14
Stiffness to Weight: Bending, points 14
25
Strength to Weight: Axial, points 9.1 to 16
20
Strength to Weight: Bending, points 11 to 15
19
Thermal Shock Resistance, points 16 to 29
12

Alloy Composition

Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.2 to 0.4
Chromium (Cr), % 0
18 to 23
Copper (Cu), % 23.5 to 25.7
0
Iron (Fe), % 0 to 0.050
60 to 73.8
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0.35 to 0.65
8.0 to 12
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 2.0
Silver (Ag), % 74 to 76
0
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 0 to 0.060
0