ASTM B780 Alloy vs. EN 1.3518 Steel

ASTM B780 alloy belongs to the otherwise unclassified metals classification, while EN 1.3518 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is EN 1.3518 steel.

ASTM B780 Silver-Copper-Nickel Electrical Contact Alloy EN 1.3518 (100CrMnSi4-4) Through-Hardening Bearing Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		83
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.36
Poisson's Ratio		0.29

Shear Modulus, GPa		30
Shear Modulus, GPa		72

Tensile Strength: Ultimate (UTS), MPa		330 to 590
Tensile Strength: Ultimate (UTS), MPa		630

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		260

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		18
Thermal Expansion, µm/m-K		13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		70 to 76
Electrical Conductivity: Equal Volume, % IACS		7.3

Electrical Conductivity: Equal Weight (Specific), % IACS		62 to 68
Electrical Conductivity: Equal Weight (Specific), % IACS		8.5

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		7.8

Common Calculations

Stiffness to Weight: Axial, points		4.5
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		14
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		9.1 to 16
Strength to Weight: Axial, points		23

Strength to Weight: Bending, points		11 to 15
Strength to Weight: Bending, points		21

Thermal Shock Resistance, points		16 to 29
Thermal Shock Resistance, points		19

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.050

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0.93 to 1.1

Chromium (Cr), %		0
Chromium (Cr), %		0.9 to 1.2

Copper (Cu), %		23.5 to 25.7
Copper (Cu), %		0 to 0.3

Iron (Fe), %		0 to 0.050
Iron (Fe), %		96.3 to 97.8

Lead (Pb), %		0 to 0.030
Lead (Pb), %		0

Manganese (Mn), %		0
Manganese (Mn), %		0.9 to 1.2

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.1

Nickel (Ni), %		0.35 to 0.65
Nickel (Ni), %		0

Oxygen (O), %		0
Oxygen (O), %		0 to 0.0015

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0
Silicon (Si), %		0.45 to 0.75

Silver (Ag), %		74 to 76
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.030

Zinc (Zn), %		0 to 0.060
Zinc (Zn), %		0