ASTM B780 Alloy vs. CC751S Brass

ASTM B780 alloy belongs to the otherwise unclassified metals classification, while CC751S brass belongs to the copper alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is CC751S brass.

ASTM B780 Silver-Copper-Nickel Electrical Contact Alloy EN CC751S (CuZn33Pb2Si-C) Leaded Brass

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		83
Elastic (Young's, Tensile) Modulus, GPa		110

Elongation at Break, %		1.1 to 9.1
Elongation at Break, %		5.6

Poisson's Ratio		0.36
Poisson's Ratio		0.31

Shear Modulus, GPa		30
Shear Modulus, GPa		40

Tensile Strength: Ultimate (UTS), MPa		330 to 590
Tensile Strength: Ultimate (UTS), MPa		450

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		190

Specific Heat Capacity, J/kg-K		270
Specific Heat Capacity, J/kg-K		390

Thermal Expansion, µm/m-K		18
Thermal Expansion, µm/m-K		20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		70 to 76
Electrical Conductivity: Equal Volume, % IACS		25

Electrical Conductivity: Equal Weight (Specific), % IACS		62 to 68
Electrical Conductivity: Equal Weight (Specific), % IACS		28

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		8.1

Common Calculations

Stiffness to Weight: Axial, points		4.5
Stiffness to Weight: Axial, points		7.2

Stiffness to Weight: Bending, points		14
Stiffness to Weight: Bending, points		19

Strength to Weight: Axial, points		9.1 to 16
Strength to Weight: Axial, points		15

Strength to Weight: Bending, points		11 to 15
Strength to Weight: Bending, points		16

Thermal Shock Resistance, points		16 to 29
Thermal Shock Resistance, points		15

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.1

Antimony (Sb), %		0
Antimony (Sb), %		0 to 0.5

Cadmium (Cd), %		0 to 0.050
Cadmium (Cd), %		0

Copper (Cu), %		23.5 to 25.7
Copper (Cu), %		62.7 to 66

Iron (Fe), %		0 to 0.050
Iron (Fe), %		0.25 to 0.5

Lead (Pb), %		0 to 0.030
Lead (Pb), %		0.8 to 2.2

Manganese (Mn), %		0
Manganese (Mn), %		0 to 0.15

Nickel (Ni), %		0.35 to 0.65
Nickel (Ni), %		0 to 0.8

Silicon (Si), %		0
Silicon (Si), %		0.65 to 1.1

Silver (Ag), %		74 to 76
Silver (Ag), %		0

Tin (Sn), %		0
Tin (Sn), %		0 to 0.8

Zinc (Zn), %		0 to 0.060
Zinc (Zn), %		27.9 to 35.6