ASTM B780 Alloy vs. Grade 3 Babbitt Metal
Both ASTM B780 alloy and grade 3 Babbitt Metal are otherwise unclassified metals. There are 9 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is ASTM B780 alloy and the bottom bar is grade 3 Babbitt Metal.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 7.4 |
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 56 |
| Latent Heat of Fusion, J/g | 140 | |
| 79 |
| Poisson's Ratio | 0.36 | |
| 0.35 |
| Shear Modulus, GPa | 30 | |
| 21 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 230 |
| Stiffness to Weight: Axial, points | 4.5 | |
| 4.2 |
| Stiffness to Weight: Bending, points | 14 | |
| 17 |
| Thermal Expansion, µm/m-K | 18 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 7.5 to 8.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.1 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 0 to 0.050 | |
| 0 to 0.050 |
| Copper (Cu), % | 23.5 to 25.7 | |
| 7.5 to 8.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.080 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 to 0.35 |
| Nickel (Ni), % | 0.35 to 0.65 | |
| 0 |
| Silver (Ag), % | 74 to 76 | |
| 0 |
| Tin (Sn), % | 0 | |
| 82.3 to 85 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 to 0.0050 |