ASTM B817 Type I vs. 383.0 Aluminum
ASTM B817 type I belongs to the titanium alloys classification, while 383.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM B817 type I and the bottom bar is 383.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 73 |
| Elongation at Break, % | 4.0 to 13 | |
| 3.5 |
| Fatigue Strength, MPa | 360 to 520 | |
| 150 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 28 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 960 | |
| 280 |
| Tensile Strength: Yield (Proof), MPa | 700 to 860 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 540 |
| Maximum Temperature: Mechanical, °C | 340 | |
| 170 |
| Melting Completion (Liquidus), °C | 1600 | |
| 580 |
| Melting Onset (Solidus), °C | 1550 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 560 | |
| 880 |
| Thermal Conductivity, W/m-K | 7.1 | |
| 96 |
| Thermal Expansion, µm/m-K | 9.6 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.0 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.0 | |
| 74 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 10 |
| Density, g/cm3 | 4.4 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 38 | |
| 7.5 |
| Embodied Energy, MJ/kg | 610 | |
| 140 |
| Embodied Water, L/kg | 200 | |
| 1030 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 120 | |
| 8.2 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2310 to 3540 | |
| 150 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 35 | |
| 50 |
| Strength to Weight: Axial, points | 48 to 60 | |
| 28 |
| Strength to Weight: Bending, points | 42 to 49 | |
| 34 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 39 |
| Thermal Shock Resistance, points | 54 to 68 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.5 to 6.8 | |
| 79.7 to 88.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chlorine (Cl), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 0 | |
| 2.0 to 3.0 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 1.3 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 9.5 to 11.5 |
| Sodium (Na), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.15 |
| Titanium (Ti), % | 87 to 91 | |
| 0 |
| Vanadium (V), % | 3.5 to 4.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 3.0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |