ASTM B817 Type I vs. 92-silver 8-tin-oxide
ASTM B817 type I belongs to the titanium alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 5 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.
For each property being compared, the top bar is ASTM B817 type I and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
Electrical Conductivity: Equal Volume, % IACS | 1.0 | |
76 to 80 |
Elongation at Break, % | 4.0 to 13 | |
32 to 34 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 120 | |
62 to 110 |
Tensile Strength: Ultimate (UTS), MPa | 770 to 960 | |
230 to 320 |
Tensile Strength: Yield (Proof), MPa | 700 to 860 | |
120 to 300 |