ASTM B817 Type II vs. 771.0 Aluminum
ASTM B817 type II belongs to the titanium alloys classification, while 771.0 aluminum belongs to the aluminum alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is ASTM B817 type II and the bottom bar is 771.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 70 |
| Elongation at Break, % | 3.0 to 13 | |
| 1.7 to 6.5 |
| Fatigue Strength, MPa | 390 to 530 | |
| 92 to 180 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 960 | |
| 250 to 370 |
| Tensile Strength: Yield (Proof), MPa | 780 to 900 | |
| 210 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 350 | |
| 180 |
| Melting Completion (Liquidus), °C | 1580 | |
| 630 |
| Melting Onset (Solidus), °C | 1530 | |
| 620 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 870 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 24 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 9.5 |
| Density, g/cm3 | 4.6 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 40 | |
| 8.0 |
| Embodied Energy, MJ/kg | 650 | |
| 150 |
| Embodied Water, L/kg | 220 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 to 120 | |
| 4.4 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2890 to 3890 | |
| 310 to 900 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 34 | |
| 46 |
| Strength to Weight: Axial, points | 55 to 58 | |
| 23 to 35 |
| Strength to Weight: Bending, points | 45 to 47 | |
| 29 to 39 |
| Thermal Shock Resistance, points | 62 to 66 | |
| 11 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.0 to 6.0 | |
| 90.5 to 92.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chlorine (Cl), % | 0 to 0.2 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.060 to 0.2 |
| Copper (Cu), % | 0.35 to 1.0 | |
| 0 to 0.1 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0.35 to 1.0 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0 | |
| 0.8 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.15 |
| Sodium (Na), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 |
| Titanium (Ti), % | 82.1 to 87.8 | |
| 0.1 to 0.2 |
| Vanadium (V), % | 5.0 to 6.0 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 6.5 to 7.5 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.15 |