ASTM B817 Type II vs. AWS BVAu-2

ASTM B817 type II belongs to the titanium alloys classification, while AWS BVAu-2 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ASTM B817 type II and the bottom bar is AWS BVAu-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
100
Poisson's Ratio 0.32
0.4
Shear Modulus, GPa 40
36
Tensile Strength: Ultimate (UTS), MPa 900 to 960
150

Thermal Properties

Latent Heat of Fusion, J/g 400
92
Melting Completion (Liquidus), °C 1580
890
Melting Onset (Solidus), °C 1530
890
Specific Heat Capacity, J/kg-K 550
180
Thermal Expansion, µm/m-K 9.9
15

Otherwise Unclassified Properties

Density, g/cm3 4.6
17

Common Calculations

Stiffness to Weight: Axial, points 13
3.3
Stiffness to Weight: Bending, points 34
9.1
Strength to Weight: Axial, points 55 to 58
2.4
Strength to Weight: Bending, points 45 to 47
3.6
Thermal Shock Resistance, points 62 to 66
7.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 6.0
0
Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.1
0 to 0.0050
Chlorine (Cl), % 0 to 0.2
0
Copper (Cu), % 0.35 to 1.0
19.5 to 20.5
Gold (Au), % 0
79.5 to 80.5
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0.35 to 1.0
0
Lead (Pb), % 0
0 to 0.0020
Nitrogen (N), % 0 to 0.040
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0
0 to 0.0020
Silicon (Si), % 0 to 0.1
0
Sodium (Na), % 0 to 0.2
0
Tin (Sn), % 1.5 to 2.5
0
Titanium (Ti), % 82.1 to 87.8
0
Vanadium (V), % 5.0 to 6.0
0
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.4
0