ASTM B817 Type II vs. Grade 20 Titanium
Both ASTM B817 type II and grade 20 titanium are titanium alloys. They have 83% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM B817 type II and the bottom bar is grade 20 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 3.0 to 13 | |
| 5.7 to 17 |
| Fatigue Strength, MPa | 390 to 530 | |
| 550 to 630 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Reduction in Area, % | 4.0 to 13 | |
| 23 |
| Shear Modulus, GPa | 40 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 960 | |
| 900 to 1270 |
| Tensile Strength: Yield (Proof), MPa | 780 to 900 | |
| 850 to 1190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 350 | |
| 370 |
| Melting Completion (Liquidus), °C | 1580 | |
| 1660 |
| Melting Onset (Solidus), °C | 1530 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 520 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.6 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 40 | |
| 52 |
| Embodied Energy, MJ/kg | 650 | |
| 860 |
| Embodied Water, L/kg | 220 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 to 120 | |
| 71 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2890 to 3890 | |
| 2940 to 5760 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 34 | |
| 33 |
| Strength to Weight: Axial, points | 55 to 58 | |
| 50 to 70 |
| Strength to Weight: Bending, points | 45 to 47 | |
| 41 to 52 |
| Thermal Shock Resistance, points | 62 to 66 | |
| 55 to 77 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.0 to 6.0 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.050 |
| Chlorine (Cl), % | 0 to 0.2 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 5.5 to 6.5 |
| Copper (Cu), % | 0.35 to 1.0 | |
| 0 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 to 0.020 |
| Iron (Fe), % | 0.35 to 1.0 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 to 0.12 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sodium (Na), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 |
| Titanium (Ti), % | 82.1 to 87.8 | |
| 71 to 77 |
| Vanadium (V), % | 5.0 to 6.0 | |
| 7.5 to 8.5 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |