ASTM B817 Type II vs. SAE-AISI 4620 Steel

ASTM B817 type II belongs to the titanium alloys classification, while SAE-AISI 4620 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM B817 type II and the bottom bar is SAE-AISI 4620 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Elongation at Break, % 3.0 to 13
16 to 27
Fatigue Strength, MPa 390 to 530
260 to 360
Poisson's Ratio 0.32
0.29
Shear Modulus, GPa 40
73
Tensile Strength: Ultimate (UTS), MPa 900 to 960
490 to 680
Tensile Strength: Yield (Proof), MPa 780 to 900
350 to 550

Thermal Properties

Latent Heat of Fusion, J/g 400
250
Maximum Temperature: Mechanical, °C 350
410
Melting Completion (Liquidus), °C 1580
1460
Melting Onset (Solidus), °C 1530
1420
Specific Heat Capacity, J/kg-K 550
470
Thermal Expansion, µm/m-K 9.9
13

Otherwise Unclassified Properties

Base Metal Price, % relative 37
3.2
Density, g/cm3 4.6
7.9
Embodied Carbon, kg CO2/kg material 40
1.6
Embodied Energy, MJ/kg 650
22
Embodied Water, L/kg 220
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26 to 120
100 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 2890 to 3890
330 to 800
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 34
24
Strength to Weight: Axial, points 55 to 58
17 to 24
Strength to Weight: Bending, points 45 to 47
18 to 22
Thermal Shock Resistance, points 62 to 66
15 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 6.0
0
Carbon (C), % 0 to 0.1
0.17 to 0.22
Chlorine (Cl), % 0 to 0.2
0
Copper (Cu), % 0.35 to 1.0
0
Hydrogen (H), % 0 to 0.015
0
Iron (Fe), % 0.35 to 1.0
96.4 to 97.4
Manganese (Mn), % 0
0.45 to 0.65
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0
1.7 to 2.0
Nitrogen (N), % 0 to 0.040
0
Oxygen (O), % 0 to 0.3
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.1
0.15 to 0.35
Sodium (Na), % 0 to 0.2
0
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 1.5 to 2.5
0
Titanium (Ti), % 82.1 to 87.8
0
Vanadium (V), % 5.0 to 6.0
0
Residuals, % 0 to 0.4
0