ASTM B817 Type II vs. C63200 Bronze
ASTM B817 type II belongs to the titanium alloys classification, while C63200 bronze belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ASTM B817 type II and the bottom bar is C63200 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 3.0 to 13 | |
| 17 to 18 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 900 to 960 | |
| 640 to 710 |
| Tensile Strength: Yield (Proof), MPa | 780 to 900 | |
| 310 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 350 | |
| 230 |
| Melting Completion (Liquidus), °C | 1580 | |
| 1060 |
| Melting Onset (Solidus), °C | 1530 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 550 | |
| 440 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 29 |
| Density, g/cm3 | 4.6 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 40 | |
| 3.4 |
| Embodied Energy, MJ/kg | 650 | |
| 55 |
| Embodied Water, L/kg | 220 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 to 120 | |
| 95 to 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2890 to 3890 | |
| 400 to 510 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.9 |
| Stiffness to Weight: Bending, points | 34 | |
| 20 |
| Strength to Weight: Axial, points | 55 to 58 | |
| 21 to 24 |
| Strength to Weight: Bending, points | 45 to 47 | |
| 20 to 21 |
| Thermal Shock Resistance, points | 62 to 66 | |
| 22 to 24 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.0 to 6.0 | |
| 8.7 to 9.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chlorine (Cl), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 0.35 to 1.0 | |
| 78.8 to 82.6 |
| Hydrogen (H), % | 0 to 0.015 | |
| 0 |
| Iron (Fe), % | 0.35 to 1.0 | |
| 3.5 to 4.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 | |
| 1.2 to 2.0 |
| Nickel (Ni), % | 0 | |
| 4.0 to 4.8 |
| Nitrogen (N), % | 0 to 0.040 | |
| 0 |
| Oxygen (O), % | 0 to 0.3 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.1 |
| Sodium (Na), % | 0 to 0.2 | |
| 0 |
| Tin (Sn), % | 1.5 to 2.5 | |
| 0 |
| Titanium (Ti), % | 82.1 to 87.8 | |
| 0 |
| Vanadium (V), % | 5.0 to 6.0 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |