ASTM Grade HF Steel vs. AISI 303 Stainless Steel

Both ASTM grade HF steel and AISI 303 stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is AISI 303 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 29
40 to 51
Fatigue Strength, MPa 200
230 to 360
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 550
600 to 690
Tensile Strength: Yield (Proof), MPa 270
230 to 420

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 1000
930
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
16
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 17
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.2
3.0
Embodied Energy, MJ/kg 46
42
Embodied Water, L/kg 150
140

Common Calculations

PREN (Pitting Resistance) 21
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
240
Resilience: Unit (Modulus of Resilience), kJ/m3 180
140 to 440
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
21 to 25
Strength to Weight: Bending, points 19
20 to 22
Thermal Diffusivity, mm2/s 4.2
4.4
Thermal Shock Resistance, points 12
13 to 15

Alloy Composition

Carbon (C), % 0.2 to 0.4
0 to 0.15
Chromium (Cr), % 18 to 23
17 to 19
Iron (Fe), % 60 to 73.8
67.3 to 74.9
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 8.0 to 12
8.0 to 10
Phosphorus (P), % 0 to 0.040
0 to 0.2
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0.15 to 0.35