ASTM Grade HF Steel vs. AWS BAg-1a

ASTM grade HF steel belongs to the iron alloys classification, while AWS BAg-1a belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is AWS BAg-1a.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
77
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 77
29
Tensile Strength: Ultimate (UTS), MPa 550
180

Thermal Properties

Latent Heat of Fusion, J/g 300
120
Melting Completion (Liquidus), °C 1410
640
Melting Onset (Solidus), °C 1370
630
Specific Heat Capacity, J/kg-K 480
280
Thermal Expansion, µm/m-K 16
22

Otherwise Unclassified Properties

Density, g/cm3 7.7
9.3
Embodied Carbon, kg CO2/kg material 3.2
48
Embodied Energy, MJ/kg 46
760

Common Calculations

Stiffness to Weight: Axial, points 14
4.6
Stiffness to Weight: Bending, points 25
15
Strength to Weight: Axial, points 20
5.4
Strength to Weight: Bending, points 19
7.6
Thermal Shock Resistance, points 12
7.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Cadmium (Cd), % 0
17 to 19
Carbon (C), % 0.2 to 0.4
0
Chromium (Cr), % 18 to 23
0
Copper (Cu), % 0
14.5 to 16.5
Iron (Fe), % 60 to 73.8
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 8.0 to 12
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 2.0
0
Silver (Ag), % 0
49 to 51
Sulfur (S), % 0 to 0.040
0
Zinc (Zn), % 0
14.5 to 18.5
Residuals, % 0
0 to 0.15