ASTM Grade HF Steel vs. AWS ER80S-B3L

Both ASTM grade HF steel and AWS ER80S-B3L are iron alloys. They have 71% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is AWS ER80S-B3L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
19
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 550
630
Tensile Strength: Yield (Proof), MPa 270
530

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
41
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 17
4.1
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.2
1.8
Embodied Energy, MJ/kg 46
23
Embodied Water, L/kg 150
60

Common Calculations

PREN (Pitting Resistance) 21
6.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 180
730
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.2 to 0.4
0 to 0.050
Chromium (Cr), % 18 to 23
2.3 to 2.7
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 60 to 73.8
93.6 to 96
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.5
0.9 to 1.2
Nickel (Ni), % 8.0 to 12
0 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0.4 to 0.7
Sulfur (S), % 0 to 0.040
0 to 0.025
Residuals, % 0
0 to 0.5