ASTM Grade HF Steel vs. EN 1.4887 Stainless Steel

Both ASTM grade HF steel and EN 1.4887 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is EN 1.4887 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 29
45
Fatigue Strength, MPa 200
280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 550
580
Tensile Strength: Yield (Proof), MPa 270
300

Thermal Properties

Latent Heat of Fusion, J/g 300
320
Maximum Temperature: Corrosion, °C 420
600
Maximum Temperature: Mechanical, °C 1000
1100
Melting Completion (Liquidus), °C 1410
1390
Melting Onset (Solidus), °C 1370
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
12
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 17
39
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 3.2
6.7
Embodied Energy, MJ/kg 46
96
Embodied Water, L/kg 150
210

Common Calculations

PREN (Pitting Resistance) 21
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
220
Resilience: Unit (Modulus of Resilience), kJ/m3 180
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 4.2
3.2
Thermal Shock Resistance, points 12
14

Alloy Composition

Carbon (C), % 0.2 to 0.4
0 to 0.15
Chromium (Cr), % 18 to 23
20 to 23
Iron (Fe), % 60 to 73.8
34.2 to 45
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 8.0 to 12
33 to 37
Niobium (Nb), % 0
1.0 to 1.5
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.0
1.0 to 2.0
Sulfur (S), % 0 to 0.040
0 to 0.015