ASTM Grade HF Steel vs. EN 1.6982 Stainless Steel

Both ASTM grade HF steel and EN 1.6982 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is EN 1.6982 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
17
Fatigue Strength, MPa 200
350
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 550
800
Tensile Strength: Yield (Proof), MPa 270
570

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
390
Maximum Temperature: Mechanical, °C 1000
770
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
25
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 17
10
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.2
2.4
Embodied Energy, MJ/kg 46
33
Embodied Water, L/kg 150
110

Common Calculations

PREN (Pitting Resistance) 21
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 180
820
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
28
Strength to Weight: Bending, points 19
25
Thermal Diffusivity, mm2/s 4.2
6.6
Thermal Shock Resistance, points 12
29

Alloy Composition

Carbon (C), % 0.2 to 0.4
0 to 0.050
Chromium (Cr), % 18 to 23
12 to 13.5
Iron (Fe), % 60 to 73.8
78.7 to 84.5
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.7
Nickel (Ni), % 8.0 to 12
3.5 to 5.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015