ASTM Grade HF Steel vs. SAE-AISI 1132 Steel

Both ASTM grade HF steel and SAE-AISI 1132 steel are iron alloys. They have 68% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is SAE-AISI 1132 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
190 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
14 to 18
Fatigue Strength, MPa 200
240 to 380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 550
640 to 720
Tensile Strength: Yield (Proof), MPa 270
350 to 590

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 17
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.2
1.4
Embodied Energy, MJ/kg 46
19
Embodied Water, L/kg 150
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
93 to 97
Resilience: Unit (Modulus of Resilience), kJ/m3 180
330 to 940
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
23 to 25
Strength to Weight: Bending, points 19
21 to 23
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12
19 to 22

Alloy Composition

Carbon (C), % 0.2 to 0.4
0.24 to 0.34
Chromium (Cr), % 18 to 23
0
Iron (Fe), % 60 to 73.8
97.8 to 98.3
Manganese (Mn), % 0 to 2.0
1.4 to 1.7
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 8.0 to 12
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0
Sulfur (S), % 0 to 0.040
0.080 to 0.13