ASTM Grade HF Steel vs. SAE-AISI S7 Steel

Both ASTM grade HF steel and SAE-AISI S7 steel are iron alloys. They have 72% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HF steel and the bottom bar is SAE-AISI S7 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 550
670 to 2030

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
40
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 17
5.0
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.2
2.3
Embodied Energy, MJ/kg 46
31
Embodied Water, L/kg 150
65

Common Calculations

PREN (Pitting Resistance) 21
8.4
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
24 to 72
Strength to Weight: Bending, points 19
22 to 46
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12
22 to 66

Alloy Composition

Carbon (C), % 0.2 to 0.4
0.45 to 0.55
Chromium (Cr), % 18 to 23
3.0 to 3.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 60 to 73.8
91.6 to 94.9
Manganese (Mn), % 0 to 2.0
0.2 to 0.9
Molybdenum (Mo), % 0 to 0.5
1.3 to 1.8
Nickel (Ni), % 8.0 to 12
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.0
0.2 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030
Vanadium (V), % 0
0 to 0.3