ASTM Grade HG10 MNN Steel vs. EN 1.4409 Stainless Steel

Both ASTM grade HG10 MNN steel and EN 1.4409 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HG10 MNN steel and the bottom bar is EN 1.4409 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
34
Fatigue Strength, MPa 170
180
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 590
490
Tensile Strength: Yield (Proof), MPa 250
220

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 500
420
Maximum Temperature: Mechanical, °C 990
990
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 21
19
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
3.7
Embodied Energy, MJ/kg 58
52
Embodied Water, L/kg 160
160

Common Calculations

PREN (Pitting Resistance) 25
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 160
120
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 3.9
4.1
Thermal Shock Resistance, points 13
11

Alloy Composition

Carbon (C), % 0.070 to 0.11
0 to 0.030
Chromium (Cr), % 18.5 to 20.5
18 to 20
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 57.9 to 66.5
61.7 to 71
Manganese (Mn), % 3.0 to 5.0
0 to 2.0
Molybdenum (Mo), % 0.25 to 0.45
2.0 to 2.5
Nickel (Ni), % 11.5 to 13.5
9.0 to 12
Niobium (Nb), % 0.2 to 1.0
0
Nitrogen (N), % 0.2 to 0.3
0 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 0.7
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.025