ASTM Grade HN Steel vs. R30003 Cobalt
ASTM grade HN steel belongs to the iron alloys classification, while R30003 cobalt belongs to the cobalt alloys. They have 52% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM grade HN steel and the bottom bar is R30003 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
210 |
Elongation at Break, % | 9.0 | |
10 to 73 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 77 | |
83 |
Tensile Strength: Ultimate (UTS), MPa | 500 | |
970 to 1720 |
Thermal Properties
Latent Heat of Fusion, J/g | 310 | |
310 |
Melting Completion (Liquidus), °C | 1400 | |
1400 |
Melting Onset (Solidus), °C | 1350 | |
1440 |
Specific Heat Capacity, J/kg-K | 480 | |
450 |
Thermal Conductivity, W/m-K | 13 | |
13 |
Thermal Expansion, µm/m-K | 16 | |
13 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 26 | |
95 |
Density, g/cm3 | 7.9 | |
8.4 |
Embodied Carbon, kg CO2/kg material | 4.6 | |
8.0 |
Embodied Energy, MJ/kg | 66 | |
110 |
Embodied Water, L/kg | 180 | |
400 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 17 | |
32 to 57 |
Strength to Weight: Bending, points | 18 | |
26 to 38 |
Thermal Diffusivity, mm2/s | 3.5 | |
3.3 |
Thermal Shock Resistance, points | 11 | |
26 to 45 |
Alloy Composition
Boron (B), % | 0 | |
0 to 0.1 |
Carbon (C), % | 0.2 to 0.5 | |
0 to 0.15 |
Chromium (Cr), % | 19 to 23 | |
19 to 21 |
Cobalt (Co), % | 0 | |
39 to 41 |
Iron (Fe), % | 44.9 to 57.8 | |
10 to 20.5 |
Manganese (Mn), % | 0 to 2.0 | |
1.5 to 2.5 |
Molybdenum (Mo), % | 0 to 0.5 | |
6.0 to 8.0 |
Nickel (Ni), % | 23 to 27 | |
14 to 16 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.015 |
Silicon (Si), % | 0 to 2.0 | |
0 to 1.2 |
Sulfur (S), % | 0 to 0.040 | |
0 to 0.015 |