ASTM Grade LC2-1 Steel vs. ASTM A387 Grade 2 Steel
Both ASTM grade LC2-1 steel and ASTM A387 grade 2 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM grade LC2-1 steel and the bottom bar is ASTM A387 grade 2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 240 | |
| 140 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 | |
| 25 |
| Fatigue Strength, MPa | 430 | |
| 190 to 250 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 810 | |
| 470 to 550 |
| Tensile Strength: Yield (Proof), MPa | 630 | |
| 260 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 450 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1470 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 46 | |
| 45 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.1 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 5.0 | |
| 2.6 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.6 |
| Embodied Energy, MJ/kg | 25 | |
| 20 |
| Embodied Water, L/kg | 60 | |
| 50 |
Common Calculations
| PREN (Pitting Resistance) | 3.1 | |
| 2.4 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 98 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1040 | |
| 180 to 320 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 29 | |
| 16 to 20 |
| Strength to Weight: Bending, points | 25 | |
| 17 to 19 |
| Thermal Diffusivity, mm2/s | 12 | |
| 12 |
| Thermal Shock Resistance, points | 24 | |
| 14 to 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.22 | |
| 0.050 to 0.21 |
| Chromium (Cr), % | 1.4 to 1.9 | |
| 0.5 to 0.8 |
| Iron (Fe), % | 92.5 to 95.3 | |
| 97.1 to 98.3 |
| Manganese (Mn), % | 0.55 to 0.75 | |
| 0.55 to 0.8 |
| Molybdenum (Mo), % | 0.3 to 0.6 | |
| 0.45 to 0.6 |
| Nickel (Ni), % | 2.5 to 3.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.4 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 to 0.025 |