AWS BAg-10 vs. 5042 Aluminum

AWS BAg-10 belongs to the otherwise unclassified metals classification, while 5042 aluminum belongs to the aluminum alloys. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is 5042 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
68
Poisson's Ratio 0.35
0.33
Shear Modulus, GPa 30
26
Tensile Strength: Ultimate (UTS), MPa 140
340 to 360

Thermal Properties

Latent Heat of Fusion, J/g 130
400
Melting Completion (Liquidus), °C 740
640
Melting Onset (Solidus), °C 690
570
Specific Heat Capacity, J/kg-K 280
900
Thermal Expansion, µm/m-K 20
24

Otherwise Unclassified Properties

Density, g/cm3 9.8
2.7

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 15
50
Strength to Weight: Axial, points 4.0
35 to 37
Strength to Weight: Bending, points 6.1
40 to 42
Thermal Shock Resistance, points 6.2
15 to 16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
94.2 to 96.8
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 19 to 21
0 to 0.15
Iron (Fe), % 0
0 to 0.35
Magnesium (Mg), % 0
3.0 to 4.0
Manganese (Mn), % 0
0.2 to 0.5
Silicon (Si), % 0
0 to 0.2
Silver (Ag), % 69 to 71
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 8.0 to 12
0 to 0.25
Residuals, % 0 to 0.15
0 to 0.15