MakeItFrom.com
Menu (ESC)

AWS BAg-10 vs. A380.0 Aluminum

AWS BAg-10 belongs to the otherwise unclassified metals classification, while A380.0 aluminum belongs to the aluminum alloys. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is A380.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
73
Poisson's Ratio 0.35
0.33
Shear Modulus, GPa 30
27
Tensile Strength: Ultimate (UTS), MPa 140
290

Thermal Properties

Latent Heat of Fusion, J/g 130
510
Melting Completion (Liquidus), °C 740
590
Melting Onset (Solidus), °C 690
550
Specific Heat Capacity, J/kg-K 280
870
Thermal Expansion, µm/m-K 20
22

Otherwise Unclassified Properties

Density, g/cm3 9.8
2.9

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 15
48
Strength to Weight: Axial, points 4.0
28
Strength to Weight: Bending, points 6.1
34
Thermal Shock Resistance, points 6.2
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
80.3 to 89.5
Copper (Cu), % 19 to 21
3.0 to 4.0
Iron (Fe), % 0
0 to 1.3
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 0.5
Silicon (Si), % 0
7.5 to 9.5
Silver (Ag), % 69 to 71
0
Tin (Sn), % 0
0 to 0.35
Zinc (Zn), % 8.0 to 12
0 to 3.0
Residuals, % 0 to 0.15
0 to 0.5