AWS BAg-10 vs. ACI-ASTM CA28MWV Steel

AWS BAg-10 belongs to the otherwise unclassified metals classification, while ACI-ASTM CA28MWV steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is ACI-ASTM CA28MWV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.35
0.28
Shear Modulus, GPa 30
76
Tensile Strength: Ultimate (UTS), MPa 140
1080

Thermal Properties

Latent Heat of Fusion, J/g 130
270
Melting Completion (Liquidus), °C 740
1470
Melting Onset (Solidus), °C 690
1430
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 20
10

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.9

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.0
38
Strength to Weight: Bending, points 6.1
30
Thermal Shock Resistance, points 6.2
40

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.2 to 0.28
Chromium (Cr), % 0
11 to 12.5
Copper (Cu), % 19 to 21
0
Iron (Fe), % 0
81.4 to 85.8
Manganese (Mn), % 0
0.5 to 1.0
Molybdenum (Mo), % 0
0.9 to 1.3
Nickel (Ni), % 0
0.5 to 1.0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
0.9 to 1.3
Vanadium (V), % 0
0.2 to 0.3
Zinc (Zn), % 8.0 to 12
0
Residuals, % 0 to 0.15
0