AWS BAg-10 vs. ACI-ASTM CD4MCuN Steel

AWS BAg-10 belongs to the otherwise unclassified metals classification, while ACI-ASTM CD4MCuN steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is ACI-ASTM CD4MCuN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.35
0.27
Shear Modulus, GPa 30
79
Tensile Strength: Ultimate (UTS), MPa 140
770

Thermal Properties

Latent Heat of Fusion, J/g 130
300
Melting Completion (Liquidus), °C 740
1420
Melting Onset (Solidus), °C 690
1380
Specific Heat Capacity, J/kg-K 280
480
Thermal Expansion, µm/m-K 20
13

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.8

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 15
25
Strength to Weight: Axial, points 4.0
28
Strength to Weight: Bending, points 6.1
24
Thermal Shock Resistance, points 6.2
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
24.5 to 26.5
Copper (Cu), % 19 to 21
2.7 to 3.3
Iron (Fe), % 0
59.5 to 66.3
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
1.7 to 2.3
Nickel (Ni), % 0
4.7 to 6.0
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 8.0 to 12
0
Residuals, % 0 to 0.15
0