MakeItFrom.com
Menu (ESC)

AWS BAg-10 vs. EN 1.8836 Steel

AWS BAg-10 belongs to the otherwise unclassified metals classification, while EN 1.8836 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is EN 1.8836 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
190
Poisson's Ratio 0.35
0.29
Shear Modulus, GPa 30
73
Tensile Strength: Ultimate (UTS), MPa 140
570

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Melting Completion (Liquidus), °C 740
1460
Melting Onset (Solidus), °C 690
1420
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 20
13

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.8

Common Calculations

Stiffness to Weight: Axial, points 4.6
13
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.0
20
Strength to Weight: Bending, points 6.1
19
Thermal Shock Resistance, points 6.2
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.015 to 0.054
Carbon (C), % 0
0 to 0.18
Chromium (Cr), % 0
0 to 0.35
Copper (Cu), % 19 to 21
0 to 0.6
Iron (Fe), % 0
95.1 to 99.985
Manganese (Mn), % 0
0 to 1.8
Molybdenum (Mo), % 0
0 to 0.23
Nickel (Ni), % 0
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.55
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.14
Zinc (Zn), % 8.0 to 12
0
Residuals, % 0 to 0.15
0