MakeItFrom.com
Menu (ESC)

AWS BAg-10 vs. SAE-AISI M3 Class 2 Steel

AWS BAg-10 belongs to the otherwise unclassified metals classification, while SAE-AISI M3 class 2 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is SAE-AISI M3 class 2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.35
0.29
Shear Modulus, GPa 30
77
Tensile Strength: Ultimate (UTS), MPa 140
770 to 2210

Thermal Properties

Latent Heat of Fusion, J/g 130
260
Melting Completion (Liquidus), °C 740
1620
Melting Onset (Solidus), °C 690
1570
Specific Heat Capacity, J/kg-K 280
440
Thermal Expansion, µm/m-K 20
12

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.3

Common Calculations

Stiffness to Weight: Axial, points 4.6
13
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 4.0
26 to 74
Strength to Weight: Bending, points 6.1
22 to 45
Thermal Shock Resistance, points 6.2
24 to 69

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
1.2 to 1.3
Chromium (Cr), % 0
3.8 to 4.5
Copper (Cu), % 19 to 21
0 to 0.25
Iron (Fe), % 0
75.8 to 82.3
Manganese (Mn), % 0
0.15 to 0.4
Molybdenum (Mo), % 0
4.8 to 6.5
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.2 to 0.45
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
5.0 to 6.8
Vanadium (V), % 0
2.8 to 3.8
Zinc (Zn), % 8.0 to 12
0
Residuals, % 0 to 0.15
0