AWS BAg-10 belongs to the otherwise unclassified metals classification, while C14500 copper belongs to the copper alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is C14500 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
120
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 30
43
Tensile Strength: Ultimate (UTS), MPa 140
220 to 330

Thermal Properties

Latent Heat of Fusion, J/g 130
210
Melting Completion (Liquidus), °C 740
1080
Melting Onset (Solidus), °C 690
1050
Specific Heat Capacity, J/kg-K 280
390
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.9

Common Calculations

Stiffness to Weight: Axial, points 4.6
7.2
Stiffness to Weight: Bending, points 15
18
Strength to Weight: Axial, points 4.0
6.8 to 10
Strength to Weight: Bending, points 6.1
9.1 to 12
Thermal Shock Resistance, points 6.2
8.0 to 12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 19 to 21
99.2 to 99.596
Phosphorus (P), % 0
0.0040 to 0.012
Silver (Ag), % 69 to 71
0
Tellurium (Te), % 0
0.4 to 0.7
Zinc (Zn), % 8.0 to 12
0
Residuals, % 0 to 0.15
0