AWS BAg-10 vs. C64210 Bronze

AWS BAg-10 belongs to the otherwise unclassified metals classification, while C64210 bronze belongs to the copper alloys. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is C64210 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
110
Poisson's Ratio 0.35
0.34
Shear Modulus, GPa 30
42
Tensile Strength: Ultimate (UTS), MPa 140
570

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Melting Completion (Liquidus), °C 740
1040
Melting Onset (Solidus), °C 690
990
Specific Heat Capacity, J/kg-K 280
430
Thermal Expansion, µm/m-K 20
18

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.4

Common Calculations

Stiffness to Weight: Axial, points 4.6
7.4
Stiffness to Weight: Bending, points 15
19
Strength to Weight: Axial, points 4.0
19
Strength to Weight: Bending, points 6.1
18
Thermal Shock Resistance, points 6.2
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
6.3 to 7.0
Arsenic (As), % 0
0 to 0.15
Copper (Cu), % 19 to 21
89 to 92.2
Iron (Fe), % 0
0 to 0.3
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.25
Silicon (Si), % 0
1.5 to 2.0
Silver (Ag), % 69 to 71
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 8.0 to 12
0 to 0.5
Residuals, % 0 to 0.15
0 to 0.5