AWS BAg-10 vs. C66900 Brass

AWS BAg-10 belongs to the otherwise unclassified metals classification, while C66900 brass belongs to the copper alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is C66900 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
120
Poisson's Ratio 0.35
0.32
Shear Modulus, GPa 30
45
Tensile Strength: Ultimate (UTS), MPa 140
460 to 770

Thermal Properties

Latent Heat of Fusion, J/g 130
190
Melting Completion (Liquidus), °C 740
860
Melting Onset (Solidus), °C 690
850
Specific Heat Capacity, J/kg-K 280
400
Thermal Expansion, µm/m-K 20
20

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.2

Common Calculations

Stiffness to Weight: Axial, points 4.6
8.1
Stiffness to Weight: Bending, points 15
20
Strength to Weight: Axial, points 4.0
15 to 26
Strength to Weight: Bending, points 6.1
16 to 23
Thermal Shock Resistance, points 6.2
14 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 19 to 21
62.5 to 64.5
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0
11.5 to 12.5
Silver (Ag), % 69 to 71
0
Zinc (Zn), % 8.0 to 12
22.5 to 26
Residuals, % 0 to 0.15
0 to 0.2