AWS BAg-10 vs. N08028 Stainless Steel

AWS BAg-10 belongs to the otherwise unclassified metals classification, while N08028 stainless steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is N08028 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
200
Poisson's Ratio 0.35
0.28
Shear Modulus, GPa 30
80
Tensile Strength: Ultimate (UTS), MPa 140
570

Thermal Properties

Latent Heat of Fusion, J/g 130
320
Melting Completion (Liquidus), °C 740
1420
Melting Onset (Solidus), °C 690
1370
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 20
16

Otherwise Unclassified Properties

Density, g/cm3 9.8
8.1

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.0
19
Strength to Weight: Bending, points 6.1
19
Thermal Shock Resistance, points 6.2
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
26 to 28
Copper (Cu), % 19 to 21
0.6 to 1.4
Iron (Fe), % 0
29 to 40.4
Manganese (Mn), % 0
0 to 2.5
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
30 to 34
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 69 to 71
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 8.0 to 12
0
Residuals, % 0 to 0.15
0